Produktdetails
Ora bright silver bath
The Ora bright bilver bath forms ductile, very bright, stress and crackfree silver coatings with a purity of at least 99.8%. Due to the extraordinary dispersion depth do the electrolyte, polishing or buffing can be eliminated for deeper layer thicknesses.
Bright Silver Bath can be used in a conventional electro-plating units. Before the electroplating procedure, the surfaced to be coated must be cleaned and degreased. To avoid non- electric silver plating with a resultant non-adhesion layer, the rectifier must be already switched on when the work pieces are being immersed in the bath.
Data:
Supply Form: make-up salt
Content (l): circa 1 l
Dangerous goods: YES
Regeneration: After analysis for silver and cyanide content, add silver salt and potassium cyanide as required.
General: For prolonged standing times, it may be necessary to rehomogenize the bath.
**The content of precious metal will be charged according to the daily quotation!
Bright Silver Bath can be used in a conventional electro-plating units. Before the electroplating procedure, the surfaced to be coated must be cleaned and degreased. To avoid non- electric silver plating with a resultant non-adhesion layer, the rectifier must be already switched on when the work pieces are being immersed in the bath.
Data:
- Silver Content** (g/l): 30.0
- Cyanide Acid Content (g/l): 120.0
- Temperature (°C): 20 -30
- Exposure Time (Min): 5– 50
- Voltage (Volt): 0.5 – 1.2
- Current Density (A/dm²): 1.0 – 1.5
- Deposition Rate (mg/Amin): 66.7
- Movement: required
- Anodes: Refined Silver
- Tank Material: Glass, alkali-resistant plastic
- Density (g/cm³): 10.3
- Hardness (HV): approx. 110
Supply Form: make-up salt
Content (l): circa 1 l
Dangerous goods: YES
Regeneration: After analysis for silver and cyanide content, add silver salt and potassium cyanide as required.
General: For prolonged standing times, it may be necessary to rehomogenize the bath.
**The content of precious metal will be charged according to the daily quotation!