The WILAPLAT Bright Silver Bath forms ductile, very bright, stress and crackfree silver coatings with a purity of at least 99.8%. Due to the extraordinary dispersion depth do the electrolyte, polishing or buffing can be eliminated for deeper layer thicknesses.
Wilaplat Bright Silver Bath can be used in a conventional electro-plating unit such as the WILAPLAT-System. Before the electroplating procedure, the surfaced to be coated must be cleaned and degreased. To avoid non- electric silver plating with a resultant non-adhesion layer, the rectifier must be already switched on when the work pieces are being immersed in the bath.

Data:

• Silver Content** (g/l): 30.0


• Cyanide Acid Content (g/l): 120.0
  
• Temperature (°C): 20 -30


• Exposure Time (Min): 5– 50


• Voltage (Volt): 0.5 – 1.2


• Current Density (A/dm²): 1.0 – 1.5


• Deposition Rate (mg/Amin): 66.7


• Movement: required


• Anodes: Refined Silver


• Tank Material: Glass, alkali-resistant plastic


• Density (g/cm³): 10.3


• Hardness (HV): approx. 110

Supply Form: make-up salt
Content (l): circa 1 l
Original Wieland n°.: 3090300202
Hazardous material: YES
Regeneration: After analysis for silver and cyanide content, add silver salt and potassium cyanide as required.

General: For prolonged standing times, it may be necessary to rehomogenize the bath.

**The content of precious metal will be charged according to the daily quotation!