Firmly adhering, hard, tarnish-resistant gold deposits are characteristic features of this bath.
In addition to the conventional metallizable materials, this bath is also suitable for the treatment of stainless steels.
The highly acidic electrolyte also has an enhanced activation power.

WILAPLAT AC 3 Pre-Plating Gold Bath is for use in conventional electro-plating units such as the WILAPLAT-System.
The pH value can be adjusted as required with diluted sulphuric acid.
A degreased surface is precondition for the
treatment.

Data:

• Gold content** (g/l): 3.0


• Temperature (°C): 20 – 30


• Exposure time (Min): 10 – 25


• Voltage (Volt): 3.0 – 4.0


• Current Density (A/dm²): 0.5 – 1.2


• Deposition Rate (mg/Amin): 16


• pH value: 1,5 – 1,8


• Movement: Movement of electrolyte or work pieces


• Anodes: Titanium, platinized


• Tank material: glass, acid resistant plastic


• Density (g/cm³): 18,2


• Hardness (HV): 110


• Layer thickness (µm): < 6

Supply form: ready for use
Content (l): 1
Regeneration: After analysis, add regeneration concentrate as required.
General note: For longer standing times, it may be necessary to rehomogenize the bath.
Hazardous material: YES


**the content of precious metal will be charged according to the daily quotation !