Ora pre-gold plating bath
This bath is characterised by firmly adhering, hard and tarnish-resistant gold deposits.
In addition to conventional metallisable materials, the bath is also suitable for stainless steels.
The strongly acidic bath also has a stronger activation capacity.
Processing is used in conventional electroplating systems. If necessary, the pH value is adjusted with diluted sulphuric acid.
A degreased surface is a prerequisite.
Data:
Delivery form: ready to use
Content (litre): 1
Regeneration: add required amount of regeneration concentrate after analysis
Dangerous goods: YES
** The precious metal content is calculated at the current daily rate!
In addition to conventional metallisable materials, the bath is also suitable for stainless steels.
The strongly acidic bath also has a stronger activation capacity.
Processing is used in conventional electroplating systems. If necessary, the pH value is adjusted with diluted sulphuric acid.
A degreased surface is a prerequisite.
Data:
- Gold content** (g/l): 3.0
- Temperature (°C): 20 - 30
- Exposure time (min): 10 - 25
- Voltage (volts): 3.0 - 4.0
- Current density (A/dm²): 0.5 - 1.2
- Deposition (mg/Amin): 16
- pH value: 1.5 - 1.8
- Movement of electrolyte or fabric
- Anodes: Titanium, platinised
- Tub material: Glass, acid-resistant plastic Plastic
- Density (g/cm³): 18.2
- Hardness (HV): 110
- Layer thickness (µm): < 6
Delivery form: ready to use
Content (litre): 1
Regeneration: add required amount of regeneration concentrate after analysis
Dangerous goods: YES
** The precious metal content is calculated at the current daily rate!